High Yield Structural Steel 600 MC Sheet is made up of low alloy cold forming material that used to be known as Domex. The material is strong, corrosion resistant and stress resistant. The most uses of the High Yield Structural 600 MC Plates are seen in the automotive and engineering industries. Suryadeep Industry is a leading supplier and Distributor of these High Yield Structural Steel S600MC Plates in various dimensions, scales and quantities. The yield strength of these plates is high at 600MPa minimum and the minimum tensile strength is in the range of 650 to 820MPa. They have good elongation properties as well. The 600 Structural Steel Plates has carbon, silicon, manganese, phosphorus, sulfur, aluminum, niobium, vanadium and titanium in its composition. The S600MC Steel Plates is made in varying thicknesses ranging from 2mm to 10mm and widths up to 1600mm with lengths ranging up to 16000mm. The specifications include EN10149-2, 10051 and 10163-2. The 600 Sheets are used in load bearing structures. There are different forms to the plates that they come in coils, slit coils or in different cut to length plates and strips.
The 600 MC High Strength Steel Plates can be cold formed and welded. They have good cutting performance. The plates could not be heat treated above 580 degrees Celsius, but can remain strong under the temperature limits. The EN 10149-2 Hot-Rolled Structural Steel Plates is very much wear and tear resistant and it could be used in applications that involve a lot of friction and wearing off. For these reasons and properties, the 600 MC Structural Steel Plates is used in construction, oil and gas industry, load bearing structures in automotive applications and in refineries. The 600 MC Plates can also be used in chemical industries, petrochemical industries and in pulp and paper production systems. Please contact us for more information on the 600 Wear Resistant Steel Plates and variations.
Table of Content - 600 MPa Coils Size Standard And Specification - MPa 600 MC Plate Chemical Resistance Guide - High Yield Structural Steel 600 Sheets Mechanical Strength Table - Most Popular Types Of S600MC High Yield Structural Steel Plate - High Yield Structural S600MC Steel Plate Material Equivalent - S600MC Structural Steel Plate Tolerances - 600 Wear Resistant Steel Plate Impact Properties - Plasma Cutting of High Yield Structural S600MC Plates - 600 MC High Yield Structural Sheet Laser Cutting - High Yield Structural 600 MC Sheet Cutting Mathod - 600 MC Plate Typical Tensile Strength - High Yield Structural S600MC Plates Thickness - S650MC Steel Plate Smallest Bending Radius - EN 10149-2 S650MC Sheet Dimensions - S650MC High Yield Structural Steel Plate Hot-rolled Slit Strip
Item | High Yield Structural 600 Plate |
Standards | EN 10149-2, EN 10051, EN 10163-2 |
Material | High Yield Structural 600 |
Thickness | 2.00-10.00 milimeter |
Width | up to 1600 milimeter |
Length | Up to 16000 milimeter |
S | C | Al | Si1 | NB | Mn | V | P | Ti |
0.010 | 0.12 |
0.015 | 0.21 |
0.09 | 1.90 | 0.20 | 0.025 | 0.15 |
Thickness (milimeter) | Elongation A v | Yield strength | Elongation A v | Tensile strength | Min. inner bending radius for a 90° bend |
2.00- 3.00 | 13 | 600 | 16 | 650- 820 | 0.7 x t |
3.01- 6 | 600 | 16 | 650- 820 | 1.1 x t | |
6.01- 10 | 600 | 16 | 650- 820 | 1.4 x t |
Thickness milimeter |
2- 10 milimeter | |
CET (CEV) | 0.21 (0.33) |
Grade | Min. impact energy for longitudinal testing, Charpy V 10x10 mm test specimens |
---|---|
High Yield Structural 600MC D | 40 J/ -20oC |
High Yield Structura® 600MC E | 27 J/ -40oC |
Cutting method | Kerf width | HAZ | Dim. tolerances |
---|---|---|---|
Plasma cutting | 2-6.5 mm | 2-5 mm | ± 1.0 mm |
Cutting method | Kerf width | HAZ | Dim. tolerances |
---|---|---|---|
Laser cutting | < 1 mm | 0.2-2 mm | ± 0.2 mm |
Cutting method | Kerf width | HAZ | Dim. tolerances |
---|---|---|---|
Oxy-fuel cutting | 2-5 mm | 4-10 mm | ± 2.0 mm |
TYPE OF STEEL | TYPICAL TENSILE STRENGTH (MPa) |
---|---|
High Yield Structural 600 MC | 760 |
THICKNESS (t) (mm) | ALONG ROLLING DIRECTION MINIMUM Ri/t | DIE OPENING WIDTH (W) MINIMUM W/t | ||
---|---|---|---|---|
HOT ROLLED STRIP | High Yield Structural 600 MC | t ≤ 3 3 < t ≤ 6 t > 6 |
0.7 1.1 1.4 |
10 10 10 |
Nom. thick. e |
smallest bending radius |
≤3 mm |
1.5 x e |
3 < e ≤ 6 mm |
2.0 x e |
> 6 mm |
2.5 x e |
Thickness in mm |
Width in mm |
2.00 – 2.99 |
900 –1300 |
3.00 – 3.99 |
900 –1450 |
4.00 – 6.00 |
900 –1500 |
Thickness in mm |
Width in mm |
|
2.50 – 2.99 |
100 – 640 |
|
3.00 – 4.60 |
100 – 690 |
|
4.61 – 6.00 |
140 – 740 |